STM Studies on Monolayers of [Co(L)4]A8 Metallogrids on Graphite
-
Semenov, Alexander; Spatz, Joachim P.; Lehn, Jean-Marie; Weidl, Christian H.; Schubert, Ulrich S.; Möller, Martin
- Abstract:
- Self-assembled tetranuclear complexes of metallogrid type wCo4L4.xPF6., R1sCH3, R2sH compound 1. and
wCo4L4.xAsF6., R1sH, R2sCH3 compound 2., Ls4,6-bis611R1-21,21-bipyrid-6-yl.-2-R2-pyrimidine were adsorbed
onto highly oriented pyrolitic graphite and studied by STM. Monodomains of a regularly packed layer of adsorbed molecules
with areas up to 0.5 mm2 were observed. Sample 1 showed a molecular pattern with nearly orthogonal periodicities of 1.35
nm=2.6 nm consisted with the size of the 2=2 Co-grid oriented normally to the surface. A periodicity of 2.5 nm=2.4 nm
was found for complex 2 consistent with orientation of the grid parallel to the surface. Holes in the monolayer, which were
formed by removal of a particular complex by STM, were observed to diffuse along the surface with a diffusion coefficient
of Ds5.2=10y16 cm2rs. The free energy of the diffusion activation were found to be DFds730 meV.
- Year:
- 1999
- Type of Publication:
- Article
- Journal:
- Applied Surface Science
- Volume:
- 144/145
- Pages:
- 456 – 460